Standard: | GB, ASTM |
---|---|
Purity: | >99.95% |
Alloy: | Alloy |
Shape: | Rectangular |
Type: | Tungsten Carbide |
Condition: | New |
Customization: |
---|
Suppliers with verified business licenses
Type | L | W | T |
LxWxT | <=610 | <=40 | <=10 |
Grade | Density (g/cm3) |
T.R.S (MPa) |
Hardness (HRA) |
Application |
YG6 | 14.8 | ≥2150 | ≥90.0 | High wear resistance, used for hard wood, used for processing original wood, aluminum section bar, brass rod and cast iron. |
YG6A | 14.9 | ≥1860 | ≥92.0 | Higher wear resistance than YG6, used for processing hard wood, original wood, aluminum section bar, brass rod and cast iron. |
YG8 | 14.8 | ≥2320 | ≥89.5 | High wear and percusstion resistance,used for processing hard wood, soft wood, ferrous and non ferrous section bars. |
YS2T | 14.8 | ≥2350 | ≥92.0 | Fine grain alloy, high wear resistance, high anti-bending strength, high resistance to bonding, high thermal strength. Machining of refractory alloys, stainless steel and high manganese steel, etc. |
TS25 | 13.8 | ≥2200 | ≥91.0 | High hardness and good wear resistance, suitable for rough turning, milling and planing of carbide steel, cast steel, high intensity steel and steel alloy. |
YL10.2 | 14.5 | ≥2150 | ≥92.2 | Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous and non-metal materials. |